Umicore DB Rhodium Concentrate


+  Ultra-bright coatings with previously unattained lightness       and brilliance +  Good covering speed +  Minor porosity +  Excellent throwing power +  Layer thicknesses of up to 5 µm can be deposited +  For rack and barrel plating +  High abrasion resistance

RHODUNA® Diamond Bright deposits brilliant-white, ultra-bright coatings of previously unattained lightness and brilliance. It is additionally characterized by high covering speed and excellent throwing power. Furthermore the RHODUNA® Diamond Bright layer thicknesses of up to 5 µm can be deposited crack-free.

Rhodium can be directly deposited on silver, gold, copper and copper alloys, nickel and nickel alloys. When plating tin, lead, zinc, aluminium and iron, intermediate nickel coatings of some µm thickness are absolutely essential. Strike nickel plating is advantageous with all substrates.

Recommended Anode – Platinum or Platinized-Titanium

 

*****WARNING*****

Plating should be performed whilst wearing a face mask or other suitably approved breathing apparatus. Plating should be performed in a suitably ventilated area or with extraction if possible. 

Supplied as a two part concentrate. Mix with Distilled Water.

$1,375.00

More info.

Make 4 payments of $343.75 over 8 weeks and get it now!





Calculate Shipping

SKU PL-00112
Unit Of Measure ea

Be The First To Review This Product!

Help other Combined Jewellery Services Pty Ltd users shop smarter by writing reviews for products you have purchased.

Write a product review

More From This Categories

COHLER CyanFree Black Solution

COHLER CyanFree Black Solution

Produces a uniform gold color. Use with a stainless steel or pure gold anode. Plate with the solution heated to 140° F (60° C) at 3 to 4 volts for 30 to 45 seconds. Changing the plating time or solution temperature will affect color. EARTHCOAT™
COHLER Cyanfree Plating Solution Pink/Rose

COHLER Cyanfree Plating Solution Pink/Rose

roduces a uniform gold color. Use with a stainless steel or pure gold anode. Plate with the solution heated to 140° F (60° C) at 3 to 4 volts for 30 to 45 seconds. Changing the plating time or solution temperature will affect color. EARTHCOAT™
COHLER Pen Plating Solution 18Y Cyanfree

COHLER Pen Plating Solution 18Y Cyanfree

COHLER Cyanfree Pen Plating Solution 18Y Use at Room Temp / Voltage 1-3 / Time: Desired Coverage
COHLER Pen Plating Solution Rose Cyanfree

COHLER Pen Plating Solution Rose Cyanfree

COHLER Cyanfree Pen Plating Solution Rose/Pink Use at Room Temp / Voltage 1-3 / Time: Desired Coverage